ANALISA KOROSI AIR RAWA DI DAERAH LASAN BAJA PADUAN RENDAH YANG TELAH DITEKUK

---

Penilaian

---

The presence of bending process lo TIG weld joint areas on low alloy Steel that has been done heat treatment can cause eraeks between the parent metal lo metal welding.. Due lo the presence of eraeks in the weld joint areas, if the specimen is operated in the acidic environment besifat specimen will be quickly attacked by corrosion. his study was conducled to analyze the corrosion that occurs in connection TIG welds that are already in the process of heat treatment guenehing and normalizing that which has been bent when immersed in aqueous media swamp. The parameters will be analyzed in this study include the corrosion rate in connection with at guenehing and normalizing been bent, corrosion behavior that occurred in connection with the parent metal, dye penetrant testing and test microstructure. From the research that increasing immersion time, the corrosion rate decreases occurring.

---

Availability

Inventory Code	Barcode	Call Number	Location	Status
1507000026	T158211	T1582112015	Central Library (References)	Available but not for loan - Not for Loan

Detail Information

Series Title

-

Call Number

T1582112015

Publisher

Indralaya : Prodi Teknik Mesin, Fakultas Teknik Universitas Sriwijaya., 2015

Collation

xix, 61 hlm. : ilus. ; tab. ; 28 cm

Language

Indonesia

ISBN/ISSN

-

Classification

620.112 230 7

Content Type

Text

Media Type

-

Carrier Type

-

Edition

-

Subject(s)

Korosi
Prodi Teknik Mesin

Specific Detail Info

-

Statement of Responsibility

DS

Other version/related

File Attachment

Comments

---

You must be logged in to post a comment